triunechem.comStandard type of epoxy vinyl ester resin
VER818 series resins are the recognized standard for epoxy vinyl ester resins. They are based on Bisphenol-A epoxy resin, and they provide resistance to a wide range of acids, alkalis, bleaches and solvents for use in many chemical processing applications. They offer excellent toughness and fatigue resistance.
|
VER818-45 |
|
|
Properties of Liquid Resin |
|
|
Type |
BPA Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
55 |
|
Viscosity (cps, 25C) |
450 |
|
Specific Gravity |
1.04 |
|
Shelf Life (months, 25C) |
9 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
12000 |
|
Tensile Modulus (10^5 psi) |
4.9 |
|
Tensile Elongation at Break (%) |
5.0-6.0 |
|
Flexural Strength (psi) |
20000 |
|
Flexural Modulus (10^5 psi) |
5.0 |
|
Heat Distortion Temperature |
108C/226F |
|
Volume Shrinkage (%) |
7.75 |
|
Barcol Hardness |
34 |
VER818-350
|
Properties of Liquid Resin |
|
|
Type |
BPA Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
55 |
|
Viscosity (cps, 25C) |
350 |
|
Specific Gravity |
1.04 |
|
Shelf Life (months, 25C) |
9 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
12500 |
|
Tensile Modulus (10^5 psi) |
5.0 |
|
Tensile Elongation at Break (%) |
5.0-6.0 |
|
Flexural Strength (psi) |
20000 |
|
Flexural Modulus (10^5 psi) |
4.85 |
|
Heat Distortion Temperature |
110C/230F |
|
Volume Shrinkage (%) |
7.5 |
|
Barcol Hardness |
34 |
Novolac type of epoxy vinyl ester resin
VER878 series resins are epoxy Novolac-based vinyl ester resins designed to provide exceptional thermal and chemical resistance properties. They offer high resistance to solvents, acids and oxidizing substances such as chlorine. They also offer high retention of strength and toughness at elevated temperatures, making them the resins of choice for flue gas applications.
|
VER878-300 |
|
|
Properties of Liquid Resin |
|
|
Type |
Novolac Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
61 |
|
Viscosity (cps, 25C) |
430 |
|
Specific Gravity |
1.06 |
|
Shelf Life (months, 25C) |
6 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
12000 |
|
Tensile Modulus (10^5 psi) |
5.15 |
|
Tensile Elongation at Break (%) |
2.5-4.0 |
|
Flexural Strength (psi) |
18500 |
|
Flexural Modulus (10^5 psi) |
5.40 |
|
Heat Distortion Temperature |
150C/300F |
|
Volume Shrinkage (%) |
8.5 |
|
Barcol Hardness |
43 |
|
VER878-400 |
|
|
Properties of Liquid Resin |
|
|
Type |
Novolac Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
65 |
|
Viscosity (cps, 25C) |
400 |
|
Specific Gravity |
1.07 |
|
Shelf Life (months, 25C) |
3-5 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
12000 |
|
Tensile Modulus (10^5 psi) |
5.15 |
|
Tensile Elongation at Break (%) |
2.2-2.8 |
|
Flexural Strength (psi) |
18500 |
|
Flexural Modulus (10^5 psi) |
5.65 |
|
Heat Distortion Temperature |
165C/329F |
|
Volume Shrinkage (%) |
9 |
|
Barcol Hardness |
43 |
|
VER878H-400 |
|
|
Properties of Liquid Resin |
|
|
Type |
Novolac Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
71.5 |
|
Viscosity (cps, 25C) |
750 |
|
Specific Gravity |
1.08 |
|
Shelf Life (months, 25C) |
3-5 |
|
Tensile Strength (psi) |
10000 |
|
Tensile Modulus (10^5 psi) |
5.45 |
|
Tensile Elongation at Break (%) |
1.5-2.5 |
|
Flexural Strength (psi) |
15500 |
|
Flexural Modulus (10^5 psi) |
5.85 |
|
Heat Distortion Temperature |
210C/410F |
|
Volume Shrinkage (%) |
9 |
|
Barcol Hardness |
52 |
Typical values, not to be construed as specifications
Brominated type of epoxy vinyl ester resin
VER858 series resins are Brominated epoxy vinyl ester resins that offer a high degree of fire retardance. They are very resistant to chemical attack by chlorine and bleach environments. Their bromine content makes them tougher and more fatigue resistant than standard epoxy vinyl ester resins.
|
VER858-40 |
|
|
Properties of Liquid Resin |
|
|
Type |
Bromintated Bisphenol-A Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
58 |
|
Viscosity (cps, 25C) |
380 |
|
Specific Gravity |
1.15 |
|
Shelf Life (months, 25C) |
6 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
12000 |
|
Tensile Modulus (10^5 psi) |
5.2 |
|
Tensile Elongation at Break (%) |
4.5-5.5 |
|
Flexural Strength (psi) |
17500 |
|
Flexural Modulus (10^5 psi) |
5.2 |
|
Heat Distortion Temperature |
106/223F |
|
Volume Shrinkage (%) |
7.75 |
|
Barcol Hardness |
40 |
|
VER858-350 |
|
|
Properties of Liquid Resin |
|
|
Type |
Bromintated Bisphenol-A Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
65 |
|
Viscosity (cps, 25C) |
300-450 |
|
Specific Gravity |
1.15 |
|
Shelf Life (months, 25C) |
9 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
12000 |
|
Tensile Modulus (10^5 psi) |
4.5 |
|
Tensile Elongation at Break (%) |
5.0-6.0 |
|
Flexural Strength (psi) |
20000 |
|
Flexural Modulus (10^5 psi) |
4.95 |
|
Heat Distortion Temperature |
116/241F |
|
Volume Shrinkage (%) |
7.5 |
|
Barcol Hardness |
35 |
|
VER858N |
|
|
Properties of Liquid Resin |
|
|
Type |
Bromintated Bisphenol-A Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
62 |
|
Viscosity (cps, 25C) |
350 |
|
Specific Gravity |
1.15 |
|
Shelf Life (months, 25C) |
4 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
11000 |
|
Tensile Modulus (10^5 psi) |
5.15 |
|
Tensile Elongation at Break (%) |
5.2-5.7 |
|
Flexural Strength (psi) |
19000 |
|
Flexural Modulus (10^5 psi) |
5.4 |
|
Heat Distortion Temperature |
130/226F |
|
Volume Shrinkage (%) |
8.5 |
|
Barcol Hardness |
42 |
Modified type of epoxy vinyl ester resin
VER Modifiled series resin is a kind VER based on Bisphenol-A epoxy vinyl ester resin and moidifled by Novolac or Elastomers that offers very high toughness, impact- and fatigue- resistance, and excellent adhesion. It is the resin of choice for demanding structural applications and as a primer for chemically resistant FRP linings.
|
VER878H-400 |
|
|
Properties of Liquid Resin |
|
|
Type |
Modified Novolac Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
71.5 |
|
Viscosity (cps, 25C) |
750 |
|
Specific Gravity |
1.08 |
|
Shelf Life (months, 25C) |
3-5 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
10000 |
|
Tensile Modulus (10^5 psi) |
5.45 |
|
Tensile Elongation at Break (%) |
1.5-2.5 |
|
Flexural Strength (psi) |
15500 |
|
Flexural Modulus (10^5 psi) |
5.85 |
|
Heat Distortion Temperature |
210C/410F |
|
Volume Shrinkage (%) |
9 |
|
Barcol Hardness |
52 |
Typical values, not to be construed as specifications
|
VER878H-400 |
|
|
Properties of Liquid Resin |
|
|
Type |
Novolac Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
71.5 |
|
Viscosity (cps, 25C) |
750 |
|
Specific Gravity |
1.08 |
|
Shelf Life (months, 25C) |
3-5 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
10000 |
|
Tensile Modulus (10^5 psi) |
5.45 |
|
Tensile Elongation at Break (%) |
1.5-2.5 |
|
Flexural Strength (psi) |
15500 |
|
Flexural Modulus (10^5 psi) |
5.85 |
|
Heat Distortion Temperature |
210C/410F |
|
Volume Shrinkage (%) |
9 |
|
Barcol Hardness |
52 |
Typical values, not to be construed as specifications
|
VER898 |
|
|
Properties of Liquid Resin |
|
|
Type |
BPA Epoxy Vinyl Ester Resin Elastomer modified type |
|
Solid Content (%) |
45 |
|
Viscosity (cps, 25C) |
400 |
|
Specific Gravity |
1.02 |
|
Shelf Life (months, 25C) |
9 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
10000 |
|
Tensile Modulus (10^5 psi) |
4.75 |
|
Tensile Elongation at Break (%) |
6.0-9.0 |
|
Flexural Strength (psi) |
16000 |
|
Flexural Modulus (10^5 psi) |
4.55 |
|
Heat Distortion Temperature |
85C/185F |
|
Volume Shrinkage (%) |
8.0 |
|
Barcol Hardness |
32 |
Typical values, not to be construed as specifications
|
VER898-1 |
|
|
Properties of Liquid Resin |
|
|
Type |
Elastomer Modified Epoxy Vinyl Ester Resin |
|
Solid Content (%) |
57 |
|
Viscosity (cps, 25C) |
400 |
|
Shelf Life (months, 25C) |
6 |
|
Physical Properties of Cured Casting |
|
|
Tensile Strength (psi) |
9594 |
|
Tensile Modulus (10^5 psi) |
4.1 |
|
Tensile Elongation at Break (%) |
12 |
|
Flexural Strength (psi) |
18406 |
|
Flexural Modulus (10^5 psi) |
4.5 |
|
Heat Distortion Temperature |
95C/203F |
|
Glass Transition, Tg2 (10K/min) |
115C/253F |
|
Barcol Hardness |
32 |