Recommended for Fiber Reinforced Materials

 

HE0201WB/HH0211WB =100/30 phr

Application:

  1. 1.For Wind turbine blades
  2. 2.Vacuum potting

Viscosity

At 25ºC , mPa.s

300

Viscosity

At 60ºC , mPa.s

50

Tg (DSC)

ºC

85-90

Flexual modulus

MPa

2826

Tensile

MPa / %

70-85

Flexural

MPa / %

115-130

Elongation at break

%

5.0

 

 

HE0201(LV)WB/HH0211WB =100/30 phr

Application:

  1. 1.For Wind turbine blades
  2. 2.Vacuum potting

Viscosity

At 25ºC , mPa.s

300

Viscosity

At 60ºC , mPa.s

50

Tg (DSC)

ºC

70-85

Flexual modulus

MPa

2800

Tensile

MPa / %

68-78

Flexural

MPa / %

115-130

Elongation at break

%

6.0

 

 

HE6802/HH6802=100/20-25 phr

Application:

  1. 1.Middle of voltage insulator and transformers.
  2. 2.Outdoor electrical insulators for medium and high voltage, such as insulators, current transformer, voltage transformer, etc
  3. 3.For mend a leak or healing of concrete, etc.
  4. 4.Vacuum potting

Viscosity

At 25ºC , mPa.s

65000-145000

Viscosity

At 60ºC , mPa.s

3500-10500

Tg (DSC)

ºC

60-80

Impact toughness

Kj/m2

8-12

Tensile

MPa / %

50-70

Flexural

MPa / %

80-100

Cure shrinkage

%

0.8-1.0

Water uptake

10 days @25 ºC,%

0.1–0.15